Introduction:
FR-110 is a binary copolymer emulsion specially developed for water-based fire retardant coatings. It has many characteristics that ordinary emulsions do not have. A large number of experiments applied to intumescent fireproof paint have proved that it has a very good match with intumescent fire-retardant systems. After the coating burns, a relatively soft and dense carbon layer is formed, which shows good fire insulation. At the same time, paint also exhibits excellent water resistance, weather resistance and storage stability. It is very suitable to be selected as the base material of waterbased steel structure fireproof paint and decorative fireproof coating.
Product Characteristics:
1. Thermal plasticity is much better than ordinary emulsion, which will not affect the activity of flame retardant. The fireproof paint will not cause carbon layer hardening and embrittlement during combustion.
2. It is used in fire-retardant coatings, and its foaming is dense after burning, and its expansion foam is better than ordinary emulsion.
3. Based on proper fireproof paint formula, it can form a more flexible and dense carbon layer after burning.
4. It has good water resistance, weather resistance and storage stability.
Application:
This product is very suitable for intumescent steel structure fireproof coating, decorative fireproof paint, textile fireproof coating, as well as water-based interior and exterior wall paint, waterproof paint, adhesive products, etc.
Technical Index |
Unit |
Target Value |
| Appearance | ------ | Transparent, glossy |
| Solid content | %（w/w） | 50±2 |
| Viscosity | mPa.s | 1000-6000 |
| pH | ------- | 4-6 |
| Density | g /cm3 | ~1.04 |
| Minimum Temperature of Film Forming | ℃ | 5 |
| Major Particle Size | nm | ~150 |
| Temperature of Glass Transition | ℃ | 28 |
Packaging and Storage:
50kg plastic drum or 1000kg IBC.